New measurements on time decrease of permeability

Abstract
The disaccommodation of Fe-Si alloys has been measured. In the region where the magnetostriction constant h1 changes sign the disaccommodation is little affected. It seems that the disaccommodation due to carbon is larger than the effect due to a corresponding atomic percentage of nitrogen, although the contrary is true for internal friction. The ratio of the diffusion coefficients of 12C and 13C in pure iron has been determined, again by measuring the disaccommodation. We find a value of (1,04 ± 0,01) in agreement with a (m)-1/2 relationship for the diffusion coefficient.

Résumé
La désaccommodation des alliages FeSi est mesurée dans le domaine où la constante de magnétostriction h1 disparaît. On trouve que cet effet a peu d'influence. Il semble que le carbone soit plus efficace que l'azote pour produire la désaccommodation, tandis que le contraire est vrai pour le frottement interne. En remplaçant le 12C par 13C le changement du coefficient de diffusion s'obtient par la mesure de la désaccommodation. On trouve une diminution de (4 ± 1) %.