Observation au microscope électronique des zones de Guinier-Preston

Abstract
Pre-precipitation phenomenon in an alloy of 4 % aluminium-copper was studied by electron microscopy and electron diffraction, in particular in the alloy aged at room temperature. The bulk samples were thinned down electrolytically after different heattreatments and observed directly by transmission. It has been possible to observe the G.-P. I zones obtained after ageing for 10 months at 25 °C, for 15 days at 75 °C and for three months at 100 °C. As regards the size of the zones, the results obtained agree well with those obtained by X-ray diffraction. Moreover, it has been observed that G.-P. I zones give the same phenomena of diffused scattering in both the electron diffraction and X-ray diffraction patterns.

Résumé
Nous avons étudié en microscopie et diffraction électroniques le phénomène de pré-précipitation dans un alliage aluminium-cuivre à 4 % et notamment dans un alliage vieilli à la température ordinaire. Les échantillons massifs, après avoir subi différents traitements thermiques, ont été amincis électrolytiquement et observés directement par transmission. Il a été possible de mettre en évidence les zones G.-P. I obtenues pour des vieillissements de 10 mois à 25 °C, de 15 jours à 75 °C et de 3 mois à 100 °C. Au point de vue de la dimension des zones, ces travaux confirment les résultats obtenus dans les études faites à l'aide des rayons X. De plus, nous avons observé que les zones G.-P. I donnaient les mêmes phénomènes de diffusion sur les diagrammes électroniques que sur les diagrammes de rayons X.