Étude de la pré-précipitation dans un alliage Al-Zn à 30 % de Zn

Abstract
The quenched alloy, aged at low temperature (from 0 to 100 °C) or annealed during very short times at higher temperature (from 150 to 200 °C) gives small angle scattering rings. Side bands are also observed on Debye-Scherrer patterns, the deviation with the solid solution line is in agreement with the radius of the ring. These effects are due to spherical pre-precipitation zones. During the annealing between 150 °C and 250 °C, one observes the precipitation of an intermediate phase which is a F. C. C. solid solution rich in Zn, appearing as epitaxial platelets on the (111) planes of the matrix.

Résumé
L'alliage trempé et vieilli à basse température (0 à 100 °C) ou revenu pendant des temps courts à température plus élevée (150 à 200 °C) donne des anneaux de diffusion centrale. En même temps, on observe sur les diagrammes Debye-Scherrer des raies satellites (side bands), dont l'écart avec la raie de la solution solide correspond au rayon de l'anneau. Ces phénomènes sont attribuables à l'existence de zones de pré-précipitation de forme sphérique. Au cours du revenu entre 150 et 250 °C on observe la précipitation d'une phase transitoire, qui est une solution solide CFC riche en Zn, sous forme de plaquettes en épitaxie sur les plans (111) de la matrice.