Formation et reversion des zones de Guinier-Preston

Alberto F. Bonfiglioli

Service de Physique des Solides, Faculté des Sciences, Orsay (Seine-et-Oise), France


Abstract
Some results obtained for Al-Zn and Al-Ag alloys by small angle scattering of X-rays, are reported. The scattering curve, typical of G.-P. zones in these alloys, has its characteristic form right from the first stages of the formation of the zones, at low temperature (from - 40 °C). Though the measured intensities are too weak to allow quantitative deductions to be made, the observed facts point to a complex structure of the zones. Some results on Al 20 % Zn alloys during reversion are also presented.


Résumé
On rapporte quelques résultats obtenus par diffusion centrale des rayons X dans le cas d'alliages Al-Zn et Al-Ag. On montre que la courbe de diffusion, typique des zones G.-P. dans ces alliages, prend sa forme caractéristique dès les premiers stades de la formation des zones, à basse température (- 40 °C environ). Bien que les intensités mesurées soient faibles et empêchent de tirer des renseignements quantitatifs valables, les faits observés font penser à une structure complexe des zones. On présente aussi quelques résultats obtenus sur un alliage Al 20 % Zn pendant la réversion.