Quenching defects in solid solutions and their effect on precipitation

R.B. Nicholson

Department of Metallurgy, University of Cambridge


Abstract
The dislocation structure of quenched aluminium alloys is very different from quenched pure aluminium. This effect has been studied by transmission electron microscopy and is probably associated with the absorption of vacancy-solute atom pairs on gliding screw dislocations and their redistribution as prismatic dislocation loops. Ageing causes precipitation on dislocations and the effects can be analysed in terms of the dislocation substructure and the misfit geometry of the precipitate and matrix lattices.


Résumé
Le réseau de dislocation dans les alliages d'aluminium trempés est très différent de celui qui existe dans l'aluminium pur trempé. Ceci a été étudié par microscopie électronique (transmission) et par dilatométrie, et cet effet est probablement lié à l'absorption de paires atome dissous - lacune par les dislocations vis qui glissent, et à leur redistribution en boucles de dislocations prismatiques. Le vieillissement entraîne la précipitation sur les dislocations et les effets peuvent être analysés à l'aide de la sous-structure de dislocations, du désaccord géométrique entre le précipité et le réseau de la matrice.

PACS
8130M - Solid-phase precipitation.
6172F - Direct observation of dislocations and other defects (etch pits, decoration, electron microscopy, x-ray topography, etc.).

Key words
aluminium compounds -- crystal defects -- heat treatment -- precipitation -- solid solutions